Sterling silver Hardness:
Dead soft Gauge/thickness:
22 ga. Form:
.025" (0.64mm) Length per weight:
29.8 ft./ozt. Weight per length:
0.034 ozt./ft. Metal color:
White Country of origin:
The term "conflict diamonds" refers to the diamond rough used to fund violent criminal insurgencies in several African countries.
The Kimberley Accord is a compact that regulates the sale and transfer of diamond rough to prevent the human destruction that conflict
diamonds cause. Rio Grande has long asked our suppliers to provide documentation proving the safe origin of the diamonds we buy.
You can be assured every diamond you buy from Rio Grande is certified “conflict-free” by both our strict standards and the Kimberley Accord.
Our Rio Graduate Gemologists are ready to help you match stones or select a specific quality. Please let them know how they can help you.
This sterling silver wire is packaged on spools, but may be coiled upon request (10-ozt. maximum per coil). It can be cut to any length that satisfies the system minimum.
Orders must weigh at least 0.01 ozt.; if you click 'Add to Cart' for a quantity less than this, the cart will offer a prompt to let you know what the minimum for this item is.
2017-2018 Gems and Findings & Display and Packaging p.24
please note: • If you order this wire coiled, be aware that its maximum coil size is 10 ozt.; we will distribute orders larger than 10 ozt. onto as many 10-ozt. coils as necessary plus a smaller coil with any remainder (for example, if you order 24 ozts. of wire, you will receive two 10-ozt. coils and one 4-ozt. coil).
• Be aware that fine-gauge wire that is normally spooled may simply be wrapped and bagged, at our discretion, when ordered in lengths less than 5 ft.
• We strive to measure quantities ordered as closely as possible; however, due to manufacturing tolerances at the mill, please allow for a ±10% variance when ordering.
How To Heat-Harden Sterling Silver
Here's how to heat-harden sterling silver to increase the strength of the metal and reduce its ductility. To harden the metal, you will be applying heat to the metal; whenever you apply heat to sterling, surround it with nitrogen, argon or forming gas or cover it with flux to prevent the metal from oxidizing. IMPORTANT: Fine silver cannot be heat-hardened. This tip is offered here courtesy of Jörg Fischer-Bühner and is reprinted from Santa Fe Symposium® Proceedings, 2003
Check the sterling for any solder joints that may already be present.
Heat the sterling to 1292°F–1346°F (700°C–730°C) for 30–60 minutes; adjusting temperatures if solder is present (if low-temperature solder is present, heat the piece only to 1000°F–1200°F). Quench in water.
Heat the sterling again, this time to 572°F (300°C), holding at that temperature for 30–60 minutes. After cooling, Vickers hardness will range between 120–140dph; if lower temperatures are used, the sterling will not achieve this level.
Annealing Sterling Silver
Learn how to anneal sterling silver, recovering metal that has become work-hardened and leaving the metal more workable.
Anneal the sterling silver between 1000°F and 1200°F (537°C and 648°C).
Heat the sterling at temperature for 30 to 60 minutes to achieve a Vickers hardness of 66–76dph.
Please Note: During annealing, protect the metal against exposure to oxygen by surrounding it with nitrogen, argon or forming gas. If this isn’t possible, protect the metal by covering it with flux contained in a stainless steel pan.
Brown & Sharpe Gauge Thicknesses
Use this handy guide to quickly, easily and accurately convert gauge sizes into inches or millimeters—or vice versa.
Heat-Hardening Sterling Silver
To harden sterling silver, heat it to 600°F (316°C) for 30–50 minutes in a kiln or furnace. Air-cool the sterling silver before pickling. The hardness will be equal to the hardness achieved by cold-working it to a 50% reduction (or ¾-hard). If you want to make your sterling silver harder than ¾-hard, you must physically reduce the cross-sectional area using the chart below.
Reduction in Cross-Sectional Area
Example: If you start with a dead-soft wire and reduce the cross-sectional area by drawing it down 50%, your material will become ¾-hard.
As a wholesale supplier to jewelers and other industry professionals, Rio Grande wants to avoid presenting wholesale pricing to retail consumers. In addition, the U.S. Patriot Act requires all suppliers of precious metals to maintain full contact information for all of its customers.
Please be aware that we vigilantly protect your account information—it will never be shared or sold to any third party for any reason, ever.
The benefits of having a dedicated account with us include:
See current pricing on all products based on published daily metal markets.
Access and print your order history and invoices any time you need them.
Create and update a 'wish' list of products you have selected but are not yet ready to purchase.
Manage and update your account information, including contact and payment information, at your convenience.